Abstract
We report on the electron tunneling characteristics on La0.7Sr0.3MnO3 (LSM) thin-film surfaces up to 580 degrees C in 10(-3) mbar oxygen pressure, using scanning tunneling microscopy/spectroscopy (STM/STS). A thresholdlike drop in the tunneling current was observed at positive bias in STS, which is interpreted as a unique indicator for the activation polarization in cation-oxygen bonding on LSM cathodes. Sr-enrichment was found on the surface at high temperature using Auger electron spectroscopy, and was accompanied by a decrease in tunneling conductance in STS. This suggests that Sr-terminated surfaces are less active for electron transfer in oxygen reduction compared to Mn-terminated surfaces on LSM. (C) 2009 American Institute of Physics. [DOI: 10.1063/1.3204022]