Abstract
Herein, the metabolites secreted by brown algae,
Cystoseira crinita
, were used as biocatalyst for green synthesis of magnesium oxide nanoparticles (MgO-NPs). The fabricated MgO-NPs were characterized using UV-vis spectroscopy, Fourier transforms infrared spectroscopy (FT-IR), Transmission Electron Microscopy (TEM), Scanning Electron Microscopy linked with energy-dispersive X-ray (SEM-EDX), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). Data showed successful formation of crystallographic and spherical MgO-NPs with sizes of 3–18 nm at a maximum surface plasmon resonance of 320 nm. Moreover, EDX analysis confirms the presence of Mg and O in the sample with weight percentages of 54.1% and 20.6%, respectively. Phyco-fabricated MgO-NPs showed promising activities against Gram-positive bacteria, Gram-negative bacteria, and
Candida albicans
with MIC values ranging between 12.5 and 50 μg mL
−1
. The IC
50
value of MgO-NPs against cancer cell lines (Caco-2) was 113.4 μg mL
−1
, whereas it was 141.2 μg mL
−1
for normal cell lines (Vero cell). Interestingly, the green synthesized MgO-NPs exhibited significant larvicidal and pupicidal activity against
Musca domestica.
At 10 μg mL
−1
MgO-NPs, the highest mortality percentages were 99.0%, 95.0%, 92.2%, and 81.0% for I, II, III instars’ larvae, and pupa of
M. domestica
, respectively, with LC
50
values (3.08, 3.49, and 4.46 μg mL
−1
), and LC
90
values (7.46, 8.89, and 10.43 μg mL
−1
), respectively. Also, MgO-NPs showed repellence activity for adults of
M. domestica
at 10 μg mL
−1
with 63.0%, 77.9%, 84.9%, and 96.8% after 12, 24, 48, and 72 h, respectively.