Abstract
The influence of colloidal TiO2 nanoparticle contents on the optical properties of poly (9,9'-di-n-octylfluorenyl-2,7-diyl) conjugated polymer (PFO) has been investigated. The solution blending method was used to prepare homogenous PFO/TiO2 nanocomposite. The nanocomposite films were prepared on glass substrates using the spin-coating technique. The films were divided into two groups, the first was left to dry at room temperature while the second was heat-treated at 120 degrees C for 1 h. Absorption and emission spectra showed that the PFO existed in alpha- and beta-phases morphology having monomeric, excimeric, and double excimeric states. In addition, both spectra revealed that TiO2 contents and heat treatment temperature extended the conjugation length of PFO. Finally, emission spectra for both cases exhibited decreasing in the line width of zero-phonon emission spectra and increasing in the vibronic splitting energy, upon increment of the TiO2, led to a significant increase in pi-electron delocalization and lower degree in chain disorder.