Abstract
A series of Mg3-xZnxFe0.5Al0.5 mixed oxide catalysts derived from hydrotalcites were tested in the ethylbenzene dehydrogenation to styrene in He atmosphere at 550 degrees C. The catalysts were prepared by coprecipitation from the nitrates of metal components followed by calcination to mixed oxides at 550 degrees C. A part of Mg2+ in Mg3Fe0.5Al0.5 mixed oxide was replaced with Zn2+ to test the effect of MgO as the support. The mixed oxides were composed of periclase and spinel-type compounds with a high surface area of 100-180 m(2) g(cat)(-1) Mossbauer and XPS measurements indicated the presence of Fe3+ on the catalysts and H-2-TPR measurement suggested that the dehydrogenation reaction is catalyzed by the reduction-oxidation between Fe3+/Fe2+. The activity of Mg3-xZnxFe0.5Al0.5 mixed oxide decreased with increasing x, indicating an important role of MgO on the activity. Both CO2-TPD measurements as well as IR measurements of adsorbed CO2 clearly indicated the presence of basic sites of Mg2+O2- on the catalysts. It seems that the combination of Mg2+O2- and Fe3+ was essential for the catalytic activity. It is concluded that the surface base sites generated on O2- bound Mg2+ near Fe3+ sites are responsible for H+-abstraction; the dehydrogenation of ethylbenzene was initiated by the H+ abstraction on Mg2+O2- basic sites, and accelerated by the reduction-oxidation of Fe3+/Fe2+ active species. (C) 2011 Elsevier B.V. All rights reserved.