Abstract
Cement and concrete are among the major contributors to CO
emissions in modern society. Researchers have been investigating the possibility of replacing cement with industrial waste in concrete production to reduce its environmental impact. Therefore, the focus of this paper is on the effective use of wheat straw ash (WSA) together with silica fume (SF) as a cement substitute to produce high-performance and sustainable concrete. Different binary and ternary mixes containing WSA and SF were investigated for their mechanical and microstructural properties and global warming potential (GWP). The current results indicated that the binary and ternary mixes containing, respectively, 20% WSA (WSA20) and 33% WSA together with 7% SF (WSA33SF7) exhibited higher strengths than that of control mix and other binary and ternary mixes. The comparative lower apparent porosity and water absorption values of WSA20 and WSA33SF7 among all mixes also validated the findings of their higher strength results. Moreover, SEM-EDS and FTIR analyses has revealed the presence of dense and compact microstructure, which are mostly caused by formation of high-density calcium silicate hydrate (C-S-H) and calcium hydroxide (C-H) phases in both blends. FTIR and TGA analyses also revealed a reduction in the portlandite phase in these mixes, causing densification of microstructures and pores. Additionally, N
adsorption isotherm analysis demonstrates that the pore structure of these mixes has been densified as evidenced by a reduction in intruded volume and a rise in BET surface area. Furthermore, both mixes had lower CO
-eq intensity per MPa as compared to control, which indicates their significant impact on producing green concretes through their reduced GWPs. Thus, this research shows that WSA alone or its blend with SF can be considered as a source of revenue for the concrete industry for developing high-performance and sustainable concretes.