Abstract
Oxide high-T-c superconductors (HTSC) are anisotropic in character since the charge carriers have free moment in the conducting CuO2 planes [A. L. Solov'ev and V. M. Dmitriev, Fiz. Nizk. Temp. 35, 227 (2009) [Low Temp. Phys. 35, 169 (2009)]] whereas their motion is impeded by insulating/partially insulating MBa2O4-delta (M = Y, Bi, Hg, Tl, CuTl, etc.) charge reservoir layers. In the transport process the charge carriers have to tunnel across insulating/partially insulating barriers along the c-axis and across the grain boundaries, which promote a fluctuation in the order parameter and in turn to the conductivity of the carriers. The studies of such fluctuation conductivity (FIC) may help in understanding the intrinsic mechanism of superconductivity. Here the electrical resistivity rho(T) versus temperature data of as-prepared and oxygen post-annealed Cu0.5Tl0.5Ba2Ca3Cu4-yZnyO12-delta (y = 0, 0.5, 1.5, 2.5) samples is studied for FIC analyses in the temperature regime well above the critical temperature; such analyses have been carried out by employing Lawrence and Doniach (LD) and Maki-Thompson (MT) models. The coherence length, inter-plane coupling, exponent, dimensionality of fluctuations and the phase relaxation time of the carriers are determined from such analyses. It is observed that the crossover temperature associated with two distinct exponents fits very well with the two-dimensional (2D) and three-dimensional (3D) LD equations. The crossover temperature T-0 is shifted to higher temperatures with enhanced Zn doping. The 3D LD region is shifted to higher temperature with the increased Zn doping. We have elucidated from these analyses that lower Tl content in the final compound may increase the charge carrier's doping efficiency of MBa2O4-delta charge reservoir layer, resulting into an increase in the coherence length along the c-axis and superconductivity parameters. A small decrease in the coherence length along the c-axis xi(c)(0) is observed in the samples with Zn doping of y = 1.5 whereas xi(c)(0) increases in the samples y = 0.5, 2.5. In comparison with as-prepared samples, the xi(c)(0) decreases after post-annealing in oxygen atmosphere. It is most likely that a decrease in the density of charge carrier's is promoted by oxygen diffusion in the unit cell may suppress the xi(c)(0). The increase oxygen diffusion is evidenced from the softening of phonon modes after post-annealing in oxygen atmosphere. The decreased population of small spins of Cu atoms induced by doping of Zn is viewed in the terms of suppression of spin gap and hence the pseudo-gap in Cu0.5Tl0.5Ba2Ca3Cu4-yZnyO12-delta (y = 0, 0.5, 1.5, 2.5) samples. (C) 2012 American Institute of Physics. [doi: 10.1063/1.3677234]