Abstract
Two mercaptobenzimidazole derivatives, namely the 1H-benzimidazol-2-thioyl hexane (MBI-C6) and the 1H-benzimidazol-2-thioyl dodecane (MBI-C12) were synthesized. The corrosion inhibiting potential of both compounds was studied in HCl solution (1.0 M HCl) for carbon steel. The investigation was conducted using gravimetric, electrochemical, Density Functional Theory (DFT), and molecular dynamics (MD) assessment methods. The carbon steel surfaces with or without the MBI-C6 and MBI-C12 were also assessed employing a Scanning Electron Microscope (SEM). The findings showed a high inhibition efficiency for both MBI-C6 and MBI-C12 at low concentrations, reaching 90% and 95.7% for MBI-C6 and MBI-C12 at 10−3 mol/L, respectively. Impedance results showed that the polarization resistance was greatly increased, from an initial value for the CS (in blank) of 12 up to 241 Ω cm2 for the inhibited solution (1.0 mol/L HCl with 10−3 mol/L of MBI-C12). Tested compounds inhibited CS corrosion through a physical-chemical adsorption mechanism that followed Langmuir adsorption isotherm model with a change in the free energy of adsorption from −35.97 to −38.63 kJ/mol. DFT calculations and MD simulations were used to check the effect of the molecular structure of MBI-C6 and MBI-C12 on their reactivity and, on the other hand, to explain their adsorption mode on the metal surface. By scanning electron microscopy (SEM), the adequate protection of carbon steel by the usage of MBI-C6 and MBI-C12 in 1.0 M HCl was confirmed. All the outcomes from experimental findings and theoretical calculations were in line.
[Display omitted]
•Benzimidazole derivatives provided higher corrosion protection for carbon steel in HCl.•Surface morphology examined by SEM confirmed the formation of inhibitor film.•Adsorption of the benzimidazole derivatives followed Langmuir isotherm model.•DFT results indicated that the long carbon chain increased the electron-donating power of MBI-C12.•MD simulations showed that both compounds exhibited a parallel adsorption on the iron surface.