Abstract
The g-C3N4/SnO2-Cu2O composite photocatalysts (PCs) were successfully synthesized via facile calcination and hydrothermal supported technique. Various analytical techniques including XRD, FT-IR, FE-SEM with EDX mapping, HR-TEM, UV–Vis DRS, PL and EIS spectra were used to exhibit the effective construction of g-C3N4/SnO2-Cu2O composite PCs. The g-C3N4/SnO2-Cu2O heterostructure composite exposed superior visible-light photo-degradation performance of methylene blue (MB) and rhodamine B (RhB) dye could be still reached 90.3% and 94.5% respectively. The upgrading of visible-light absorption, reduced the bandgap, promoting the charge separation ability and also strong-coupling heterostructured interface among g-C3N4 to SnO2-Cu2O, which were accountable for the development of the photocatalytic performance. The photo-degradation rate constant of g-C3N4/SnO2-Cu2O PCs was calculated to be 3.86 folds greater for MB (0.0282 min−1) and 4.68 folds greater for RhB dye (0.0328 min−1) compared to pristine g-C3N4, hence verifying its beneficial photocatalyst for cationic and also an anionic dyes removal. However, OH− and h+ are the predominant redox species accountable for the major impact of the MB aqueous dye photo-degradation process. This study delivers a facile and suitable way to make a visible-light active photocatalyst capable property for prospective practical application in environmental protection.
[Display omitted]
•Efficient g-C3N4/SnO2-Cu2O photocatalyst was well prepared by a facile method.•Rate constant was 3.86 and 4.68 folds higher for MB and RhB dye to pristine g-C3N4.•The g-C3N4/SnO2-Cu2O photocatalyst is apt for both anionic and cationic dyes.•Optimum photocatalyst was great stable after the five successive reusability.•OH− and h+ are the prime active species in the MB dye photo-degradation process.