Abstract
In this study, the fabrication and thermo-mechanical characteristics of glass fiber/vinyl ester composite materials for 2.4 m wind turbine rotor blade with tower height of 6 m are investigated. Hand lay-up technique with matching molds was used to produce the wind rotor blades according to National Advisory Committee for Aeronautics (NACA) 4527 aerofoil profile. Bending stiffness was found to be 14.80 kN/m. Results demonstrate the manufactured composite rotors process to manufacture wind turbine blades with structural integrity. Dynamic testing was performed to verify the structural integrity of wind turbine at 400 r.p.m. In dynamic mechanical testing, the storage modulus decreases with increase in temperature. The glass transition temperature of glass fiber/vinyl ester composite was obtained at 73.4 degree C based on loss modulus behavior. FT-IR analysis of cured vinyl ester (Hetron 922) showed presence of acrylol double bound confirming proper curing of vinyl ester. FT-IR analysis at temperature 25, 50 and 100 degree C does not show significant change in resin chemical structure. Glass fiber/vinyl ester composites exhibit approximately 23 degree C higher decomposition temperature than neat vinyl ester using thermogravimetric analyzer. Eco audit study showed that the energy and carbon emission are mainly due to use phase. It is found that materials phase has 6.1% CO2.