Abstract
A facile method was used for the synthesis of peanut-shaped very emissive NaGdF4:Yb, Er upconversion nanospheres (UCNSs) at lower temperatures with uniform size distribution. Crystallographic structure, phase purity, morphology, thermal robustness, biocompatibility, colloidal stability, surface chemistry, optical properties, and luminesce properties were explored by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), zeta potential, thermogravimetric/differential thermal analysis (TGA/DTA), Fourier-transform infrared (FTIR), ultraviolet (UV)-visible and photoluminescence spectroscopic tools. XRD pattern verified the construction of a single-phase, highly-crystalline NaGdF4 phase with a hexagonal structure. Peanut-shaped morphology of the sample was obtained from SEM micrographs which were validated from high-resolution TEM images, to have an equatorial diameter of 170 to 200 nm and a length of 220 to 230 nm, with irregular size, monodispersed, porous structure, and rough surface of the particles. The positive zeta potential value exhibited good biocompatibility along with high colloidal stability as observed from the absorption spectrum. The prepared UCNSs revealed high dispersibility, irregular size peanut-shaped morphology, rough surface, good colloidal stability, and excellent biocompatibility in aqueous media. A hexagonal phase NaGdF4 doped with ytterbium (Yb) and erbium (Er) UCNSs revealed the characteristics of highly dominant emissions located at 520-525, 538-550, and 659-668 nm corresponding to the H-2(11/2) -> I-4(15/2), S-4(3/2) -> I-4(15/2), and F-4(9/2) -> I-4(15/2) transition of Er3+ ions, respectively, as a result of energy transfer from sensitizer Yb3+ ion to emitter Er3+ ion.