Abstract
This study aimed to evaluate and compare the fatigue resistance of ProTaper Gold (PTG) and ProTaper Universal (PTU) in artificial single and double curvature canals in 5% sodium hypochlorite (NaOCl) at body temperature (37 °C). PTG and PTU files (size F1) were subjected to fatigue tests in two different artificial ceramic canals. The single curvature model had a 60° curvature angle with a 5 mm radius. The double curvature model had a 60° curvature angle with a 5 mm radius and a second 30° curvature with a 2 mm radius. A file segment was introduced into the artificial canal and immersed in water or 5% NaOCl at 37 °C. The total number of cycles to fracture (NCF) was recorded. Data were analyzed using
t
-test and linear regression analysis. The NCF of all files was significantly influenced by the type of NiTi metal alloy (
P
< .01), canal curvatures (
P
< .01), and the environmental conditions (
P
< .05). PTG had higher fatigue resistance than PTU files in both single and double curvature canals (
P
< .05). The NCF of PTU files in 5% NaOCl was shorter than that in water (
P
< .05). The mean length of broken PTG was significantly shorter than those of PTU files in both single and double curvature canals (
P
< .01). The fatigue performance of PTG is better than that of PTU in both single and double curvature. Environmental conditions may affect the fatigue behavior of PTU files with single curvature.
ProTaper Gold (PTG) and ProTaper Universal (PTU) files (size F1) were subjected to fatigue tests in two different artificial ceramic canals. The single curvature model had a 60° curvature angle with a 5 mm radius. The double curvature model had a 60° curvature angle with a 5 mm radius and a second 30° curvature with a 2 mm radius. A file segment was introduced into the artificial canal and immersed in water or 5% sodium hypochlorite (NaOCl) at 37 °C. The total number of cycles to fracture (NCF) of all files was significantly influenced by the type of NiTi metal alloy (
P
< .01), canal curvatures (
P
< .01), and the environmental conditions (
P
< .05). PTG had higher fatigue resistance than PTU files in both single and double curvature canals (
P
< .05). The NCF of PTU files in 5% NaOCl was shorter than that in water (
P
< .05). The mean length of broken PTG was significantly shorter than those of PTU files in both single and double curvature canals (
P
< .01). The fatigue performance of PTG is better than that of PTU in both single and double curvature. Environmental conditions may affect the fatigue behavior of PTU files with single curvature.
Image 1
•
PTG has higher fatigue resistance than PTU files in both single and double curvature canals.
•
The total number of cycles to fracture (NCF) of PTU files in 5% NaOCl is shorter than that in water.
•
The NCF of all files was significantly influenced by the type of NiTi metal alloy, canal curvatures, and the environmental conditions.