Abstract
► The mechanism of finger-like voids in ceramic membranes was studied in details. ► Distinguishing features of viscous fingering were observed experimentally. ► The viscous fingering phenomenon is revealed for the formation of finger-like voids.
The formation mechanism of phase-inversion ceramic hollow fibre membranes has not been well understood. In this paper, we report on the formation of finger-like macrovoids during non-solvent-induced phase inversion of alumina/PES/NMP suspensions. A membrane structure without such finger-like macrovoids was observed when the suspension was slowly immersed into pure ethanol or a mixture of 70wt% NMP and 30wt% water, whereas finger-like macrovoids occurred when the suspension was slid into the non-solvents at higher speeds. We found that the formation process of finger-like macrovoids could be fully or partially reversed when nascent membranes were taken out from water shortly after immersion, depending on the duration of the immersion. Splitting of the fingers during the formation of the macrovoids was also observed during the phase inversion of two alumina/PES/NMP suspensions. These experimental observations were not predicted by current theories of finger-like macrovoid formation in polymer membranes, but appear to mimic the well-known viscous fingering phenomenon. We therefore propose that in the phase inversion of ceramic suspensions, the viscous fingering phenomenon is an important mechanism in the formation of finger-like voids.