Abstract
The F doped TiO2/SiO2 composition oxides were prepared by sal-gel method using HF solution as fluorine source. The prepared powders were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS), Brunauer-Emmett-Teller (BET), ultraviolet-visible absorption spectroscopy (UV-Vis), photoluminescence spectroscopy (PL), Fourier transform infrared spectroscopy (FT-IR) and ammonia adsorption and temperature-programmed desorption (NH3-TPD). The photocatalytic activities of the powders for acrylonitrile degradation have been inspected. The results show that the presence of SiO2 as a support for TiO2 loading benefits the formation of the nanoparticles with a large surface. In situ IR and NH3-TPD investigation shows that the higher photocatalytic activity for F doped samples is attributed to the increase of number and strength of surface acid sites. The highest photcatalytic activity for acrylonitrile degradation is obtained for a sample calcined at 450 degrees C with molar ratio (HF to Ti) of 1.1 and 36% TiO2 loading. The degradation ratio of acrylonitrile can reach to 66% under simulant solar light for 6 min, indicating the effectiveness of photocatalytic degradation acrylonitrile using F doped TiO2/SiO2 composite oxide. (C) 2014 Elsevier B.V. All rights reserved.