Abstract
Aims and Objectives: To evaluate the influence of indirect chair-side polymerization of resin composite cores on the fracture resistance of overlaying IPS e.max Press crowns.
Materials and Methods: Root canals of 60 extracted premolars were prepared to receive #2 fiber posts after the crowns were sectioned 2 mm above the cervical line. In Groups 1u3 (n = 10 each), posts were luted to the prepared dowel spaces using self-adhesive resin cement. Resin composite cores were then bonded and incrementally built-up using Filtek Z250 XT, Filtek P60, and Filtek P90 resin composites. In Groups 4u6 (n = 10 each), the fabricated post-core systems were subjected to post-curing heat and pressure treatment before cementation to their respective teeth using self-adhesive resin cement. Another 10 sound premolars served as control. All teeth in the test and control groups were then subjected to standardized preparation to receive IPS e.max Press crowns before testing their fracture resistance and the mode of restorations' failure. The collected results were statistically analyzed using ANOVA, KruskaluWallis, and Tukey's tests on the past software used at alpha = 0.05 to stand on the significance of the detected differences.
Results: Significant differences were detected between the fracture resistance of teeth in different groups (ANOVA, P = 2.857E-35). Crowns in Groups 4u6 provided higher fracture resistance than those in Groups 1u3 (Tukey's test, P < 0.05). Crowns in Groups 4 and 6 provided higher fracture resistance than the control, while those in Groups 2 and 3 provided lower fracture resistance than the control (Tukey's test, P < 0.05).
Conclusion: Indirect composite cores improved the fracture resistance of IPS e.max Press crowns when compared to directly fabricated post and cores. The directly and indirectly polymerized nanohybrid, methacrylate-based composite (Filtek Z250 XT) cores yielded the highest fracture resistance for the utilized all-ceramic crowns.