Abstract
This paper presents investigations on the tribological behaviour of PTFE composites against steel at cryogenic temperatures. The results showed that the friction coefficient decreases with temperature down to 77 K, but did not follow a linear evolution further down to extreme low temperatures. It can be stated that the cryogenic environment has a significant influence on the tribological performance of the polymer composites. The effect of low temperatures was more clearly detected at low sliding speed, where friction heat is reduced. A change in wear mechanism from adhesive to abrasive was observed in this case. SEM and AFM analyses showed that the PTFE matrix composites investigated under these experimental conditions have transferred material onto the disc down to very low temperatures. Chemical analyses indicate the presence of iron fluorides.