In this work, the effect of the thermal annealing atmosphere on the structural, optical and electrical properties of the sulfosalt SnSb2S4 films obtained by thermal vacuum evaporation was studied. The samples are annealed at different atmospheres in the temperature range 50-275 degrees C for 1 h. It is observed that SnSb2S4 films exhibit a dramatic change in their electrical properties at transition temperatures of about 150 degrees C, 170 degrees C and 200 degrees C after an annealing process under air, nitrogen and vacuum atmospheres, respectively. The electrical resistivity measurements suggest that obtained films show 'semiconducting' behavior with resistivities between 10 and 100 Q cm; the annealed films present rather lower resistivities between 10(-2) and 10(-3) Omega cm and exhibit obvious p(+)-type semiconductor behavior with a dominant crystalline component. (C) 2011 Elsevier B.V. All rights reserved.