Abstract
Aqueous hybrid supercapacitors (AHSCs) exhibit promising electrochemical performance with long cyclic stability and high power density. However, the low-energy density restricted their development to commercialization. To improve the energy density, we proposed a heterostructured (HS) composite of nickel–cobalt–sulfide (NCS) nanoflowers embedded in exfoliated Ti3C2Tx−MXene layers (HS−NCS@MXene). The NCS nanoflowers were uniformly dispersed inside the MXene layers and formed a sandwich-like structure. The HS−NCS@MXene exhibited remarkable pseudocapacitive performance in a three-electrode system. The capacitance can reach 2637 F g−1 (1582 C g−1) at 2.5 A g−1 with stable cycling life over 10,000 cycles and retained 96% capacity of the initial value. Post−mortem investigations confirmed that the charge storage mechanism in HS−NCS@MXene composite is a combination of Faradic and electrochemical double-layer storage. An AHSC was assembled by coupling the HS−NCS@MXene as a positive electrode and activated carbon as a negative electrode (HS−NCS@MXene//AC–AHSC). The HS−NCS@MXene//AC–AHSC can operate in a potential range up to 1.6 V and deliver a high capacitance of 226 F g−1 at 1.5 A g−1 with stable cyclic life (92%) up to 20,000 cycles. Moreover, the HS−NCS@MXene//AC−AHSC also possessed a high energy density of 80 Wh kg−1 at a power density of 1196 W kg−1, which exceeds most recently published works. The synergistic effect of NCS and MXene enables the HS−NCS@MXene composite to deliver outstanding electrochemical performance for AHSCs.
To realize highly efficient aqueous hybrid supercapacitor, HS−NCS@MXene electrode with multi-component and rational morphological architectures is proposed. The HS−NCS@MXene electrode demonstrates remarkable pseudocapacitive performance in a three- and two electrode systems with reduced ionic diffusion paths. [Display omitted]
•Nickel-cobalt-sulfide-nanoflowers in-situ embedded in Ti3C2Tx–MXene layers to construct heterostructured electrode.•The HS–NCS@MXene electrode exhibits exceptional high–capacitance of 2637 F g–1 at 2.5 A g–1 with superb rate-capability.•The HS–NCS@MXene//AC-AHSC shows good performance by achieving a high capacitance of 226 F g–1 at 1.5 A g–1.•The HC–NCS@MXene//AC–AHSC delivers high-energy/power densities (80 Whkg–1 @ 1196 Wkg–1) super-long life up to 20k cycles.