Abstract
Electrocatalytic reduction of nitrite to NH3 provides a new route for the treatment of nitrite in wastewater, as well as an attractive alternative to NH3 synthesis. Here, we report that an oxygen vacancy-rich TiO2-x nanoarray with different crystal structures self-supported on the Ti plate can be prepared by hydrothermal synthesis and by subsequently annealing it in an Ar/H2 atmosphere. Anatase TiO2-x (A-TiO2-x) can be a superb catalyst for the efficient conversion of NO2- to NH3; a high NH3 yield of 12,230.1 +/- 406.9 mu g h-1 cm-2 along with a Faradaic efficiency of 91.1 & PLUSMN; 5.5% can be achieved in a 0.1 M NaOH solution containing 0.1 M NaNO2 at -0.8 V, which also exhibits preferable durability with almost no decay of catalytic performances after cycling tests and long-term electrolysis. Furthermore, a Zn-NO2- battery with such A-TiO(2-)x as a cathode delivers a power density of 2.38 mW cm-2 as well as a NH3 yield of 885 mu g h-1 cm-2.