Abstract
Objective: To investigate the flexural strength of hot isostatically pressed nano 3 mol% yttria partially stabilised zirconia and conventionally sintered micro 3 mole% yttria partially stabilised zirconia. Methods: A total of 40 bar-shaped (2 mm x 4 mm x 16 mm) specimens were prepared from hot isostatically pressed nano 3 mol% yttria partially stabilised zirconia (CeramaZirc Nano HIP, Precision Ceramics) and conventionally sintered micro 3 mole% yttria partially stabilised zirconia (CeramaZirc, Precision Ceramics). Two groups were prepared for each material (n = 10), with one serving as 'control' and the other being cyclically loaded using a chewing simulator (7 kg; 250 k cycles): SEM imaging was also undertaken on selected specimens. Flexural strength until fracture was recorded (ISO 6872). Paired and unpaired t-tests were chosen to compare mean outcomes between the four groups (p < 0.05). Results: Significant statistical difference was only found between the means of control specimens. CeramaZirc Nano HIP had the highest mean value (1048.9 MPa), whilst the lowest was seen for CeramaZirc after loading (770 MPa). Values for both materials were higher without loading than after loading. Values after cyclical loading showed large SD values (276.2-331.8) in comparison to 'control' (66.5-100.3). SEM imaging after cyclical loading revealed a smoother and less destructed surface of CeramaZirc Nano HIP compared to CeramaZirc. Significance: HIP nano zirconia exhibited inferior strength, surface polishability and behaviour to loading. Therefore, further investigation on the behaviour of such materials should be conducted before recommending for clinical use.