Abstract
•Supperalloy good resistance to high temperature oxidation.•Ni-base alloy IN738 and Inconel 617 good resistance to hot corrosion.•Corrosion resistance of supperalloys depending on environment of abrasive ions such as (NaCl or NaSO4).•Hot corrosion resistance depend on what the oxides phases where formed.
Superalloys are extensively used at high temperature applications due to their good oxidation and corrosion resistance properties in addition to their high stability were made at high temperature. Experimental measurements of hot corrosion at high temperature of Inconel 617 and Inconel 738 superalloys. The experiments were carried out at temperatures 700°C, 800°C and 900°C for different exposure times to up to 100h. The corrosive media was NaCl and Na2SO4 sprayed on the specimens. Seven different specimens were used at each temperature. The corrosion process is endothermic and the spontaneity increased by increasing temperature. The activation energy was found to be Ea=23.54 and Ea=25.18KJ/mol for Inconel 738 and Inconel 617 respectively. X-ray diffraction technique (XRD) was used to analyze the formed scale. The morphology of the specimen and scale were examined by scanning electron microscopy (SEM). The results show that the major corrosion products formed were NiCr2O4, and Co Cr2O4 spinles, in addition to Cr2O3.