Nanoadhesives of epoxy resin are synthesized and evaluated. It is organically modified by multiwalled carbon nanotubes (MWCNT) (1% by weight) as reinforcement. Tensile tests are conducted on multiple identical unnotched and notched specimens to evaluate the overloading and fracture behavior of the nanoadhesives and are then compared with the neat epoxy resin. In comparison with the neat epoxy, it is found that the 1% MWCNT reinforcement increased the ultimate and residual strength by about 29 and 56%, respectively. In comparison with the neat resin, there is a 265% increase in the fracture toughness of the MWCNT adhesive. Fracture surface analysis revealed the various mechanisms by which the MWCNT adhesive acquire its superior strength and toughness in comparison with the neat resin.