Abstract
The current study was carried out with a view to investigating the influence of age-hardening parameters, aging temperature and time, on the tensile properties and quality indices of a high-strength Al-9 pct Si casting alloy, namely, 354-Al-9 pct Si-1.8 pct Cu-0.5 pct Mg. Quality charts were used as an evaluation tool for selecting the optimum conditions to be applied, in practice, in order to develop high strength and optimum quality in 354 casting alloy. Aging at a low temperature of 428 K (155 A degrees C) was observed to produce the greatest strength and optimum quality in the 354-type castings compared to aging at higher temperatures. The peak strength observed for 354 alloy may be attained after shorter aging times on the condition that the aging temperature is increased. The aging times required for reaching peak strength in 354 alloys are 72 hours, 40 hours, 8 hours, 1 hour, and 15 minutes at aging temperatures of 428 K, 443 K, 468 K, 493 K, and 518 K (155 A degrees C, 170 A degrees C, 195 A degrees C, 220 A degrees C, and 245 A degrees C), respectively. Aging treatment at higher temperatures is accompanied by a reduction in the tensile properties and quality index values of the castings; however, it also introduces the possibility of a significant economical strategy for minimizing the time and the cost of this same treatment. Aging treatment at a lower temperature of 428 K (155 A degrees C) produces fine and dense precipitates displaying smaller interparticle spacing, while at higher aging temperatures, such as 518 K (245 A degrees C), the precipitates are coarser in size, less dense, and more widely dispersed. The quality charts developed in the course of the current research facilitate the interpretation and evaluation of the tensile properties of the 354 alloy. Such charts provide a logical evaluation tool, from the metallurgical point of view, for an accurate prediction of the influence of aging parameters studied on the properties of the alloys. Depending on the required level of tensile properties and based on the quality charts developed, it is possible to make a rigorous selection as to the most suitable aging parameters to be applied to the 354 alloy so as to obtain the best possible cost-effective compromise between alloy strength and quality.