Abstract
Here we investigate the effects (thermal, microstructural, and creep properties) of adding Sb2O3 nanoparticles to a hypoeutectic Sn-5 wt% Bi solder alloy. The Sb2O3-containing solder alloy was prepared by mechanically incorporating 0.5 wt% Sb2O3 nanoparticles into the Sn-5 wt% Bi solder alloy. The addition of nano-sized Sb2O3 particles to the Sn-Bi solder alloy increases the melting temperature, but only slightly. The main phases of the investigated solder alloys include the beta-Sn and Bi-rich phases in addition to the crystalline phase of Sb2O3 nanoparticles. No other intermetallic compounds were observed in the beta-Sn matrix. The tensile creep experiments have been carried out in the 303-363 K temperature interval under constant stresses ranging from 5.1 to 7.64 MPa. The creep parameters of both solders increased gradually with increasing creep temperature up to 333 K, after which they increased rapidly with relatively higher values. The creep parameters of the Sb2O3-containing solder alloys are smaller than that of Sb2O3-free solder alloys. The present solder alloys exhibit class-M creep behavior. The calculated stress exponent values and activation energy data for both solders could be related to dislocation climb through core diffusion as the dominant operating mechanism.