Abstract
In this study, we investigated the preparation conditions of titanium nitride (TiN) through nitridation of nanosized titanium dioxide (TiO2) without particle agglomeration. Synthesis of nanocrystalline TiN powder was attempted via ammonia (NH3) nitridation of nanocrystalline TiO2 powder. The nitridation behavior was investigated using thermogravimetry (TG) in an NH3 atmosphere. Non-isothermal TG experiments showed that nitridation of the nanocrystalline TiO2 powder began at similar to 750 degrees C. Two types of experiments were performed using isothermal TG. In the first experiment, an argon atmosphere was used while heating at 5 degrees C/min. On reaching the holding temperature (900 or 1,000 degrees C), the atmosphere was changed to NH3/Ar (50/50 kPa). This atmosphere was used throughout the second experiment. The first experiment produced a nitride ponder with severely agglomerated particles. In the second experiment, nano-sized powder particles with inhibited agglomeration were obtained, and long holding time of 6 h at 900 or 1,000 degrees C was effective in obtaining the small nitrided particles. (C) 2019 The Ceramic Society of Japan. All rights reserved.