Abstract
Two structurally different plasticizers (cyclic and linear) and the effect of cryogenic grinding on the solidification behavior at high cooling rates by a continuous cooling transformation approach of poly(butylene terephthalate)/poly(ethylene terephthalate), PBT/PET, blends are described. The solidification curve (density versus cooling rate) is confirmed as an effective tool to compare the differences in crystallization behavior under conditions mimicking processing. In comparison to the bulky cyclic plasticizer, the linear oligomeric one was found to have a more pronounced influence on the crystallization behavior. A 60/40 by weight PBT/PET blend shows a drop-off of density at similar to 50 K/s. In the plasticized sample, the long-range crystalline order appears up to a cooling rate of similar to 250K/s, making the blend comparable to pure PBT. Grinding the components before blending further improves crystallizability and synergy to the addition of the plasticizer. The results suggest the important role of local chain mobility in the solidification behavior at high cooling rates. (C) 2015 Wiley Periodicals, Inc.