Abstract
Objectives: To evaluate the effect of silane application and silane heat treatment on lithium-disilicate ceramic when bonded to composite resin.
Methods: Twelve blocks of lithium-disilicate (LD) ceramic were fabricated and bonding surfaces were etched using 9.5% hydrofluoric acid (90 seconds). Three experimental groups resulted from the various surface treatment combinations, which included, no silane application (NS) (controls), silane application (S) and silane heat treatment (HS) (100 degrees C for 5 minutesutes). Ceramic and composite resin blocks were bonded using an adhesive resin and light cured restorative composite as a luting agent, under standard conditions. A total of 90 specimen sticks (8 x 1mm(2)) were subjected to micro-tensile bond strength testing. The means of micro-tensile bond strength (mu-tbs) of the study groups were analyzed using t-test and ANOVA. The tested specimens were analyzed for mode of failure using scanning electron microscopy (SEM).
Results: The highest mu-tbs value (42.6 +/- 3.70 MPa) was achieved for LD ceramics with heat-dried silane. Both silane application and heat treatment of silane resulted in significant (p<0.05) improvements in microtensile bond strength of LD ceramics when bonded to resin composite.
Conclusions: The application of silane and its heat treatment showed significant improvement in bond strength of lithium disilicate ceramic when bonded to composite.