Abstract
The magnetic behavior of titanium dioxide nanobelts has been investigated with and without Co doping. Room temperature ferromagnetism was observed when the Co-doped anatase TiO(2) nanobelts were prepared via vacuum annealing of 2.5 at. % Co-doped titanate nanobelts, while annealing them in air resulted in paramagnetic ordering. Interestingly, by vacuum annealing the undoped titanate nanobelts under the same conditions, superparamagnetic ordering was observed in the resulting anatase TiO(2) nanobelts. The electron paramagnetic resonance of this latter sample shows a strong symmetrical signal at g = 2.003 suggesting some sort of exchange interactions among the localized electrons' spin moments from single electron trapped in oxygen vacancies. (C) 2008 American Institute of Physics.