Abstract
The two-step thermal polymerization and solvothermal approach is used to construct nano heterostructures of FCN and BiOI (bismuth oxeye iodide), both of which are Nobel metal-free materials. This work reports the effect nano-heterostructure on the micro-structural, light absorption capability, PEC properties and pollutant degra-dation efficiency of the synthesised heterostructures. The addition to that formation of FCN/BiOI nano-heterostructure enhances the solar light absorption. The FCN/BiOI nano heterostructure shows 10 times higher photocurrent density than the BCN nanostructure and 3.8 time higher that FCN. The FCN/BiOI has a high induced photo-current density (20.17 mA/cm2) and H2 evolution rate (3762 mu mol h-1 cm -2) under solar light illumination (lambda >= 420 nm) in comparison with the other. Furthermore, the photocatalytic performance of this material for the breakdown of methyl red dyes was much greater. Under solar light irradiation, the azo dyes were degraded in 90 min. The FCN/BiOI nano-heterostructure has a higher dye degradation efficiency of 97.91%. The rapid transport of photo-induced electrons in the FCN/BiOI nanocomposite is responsible for the improvement in PEC and PC performances. These impressive findings suggest that this nanocomposite might be used to facilitate the PEC water splitting and the PC degradation of MR in the presence of light. The current research provides insight on how to best tailor composition and structure for efficient FCN photo-electrocatalysis water splitting and Methyl red dye degradation.