Abstract
We have investigated the impact of AlN buffer layer growth parameters for developing highly single crystalline AlGaN films. The low mobility of Al adatoms and high temperature for compound formation are amongst the major causes that affects the growth quality of AlGaN films. Thus, proper optimization need to be carried out for achieving high quality AlGaN due to an augmented tendency of defect generation compared to GaN films. Thus, growth conditions need to be amended to maximize the incorporation ability of adatoms and minimize defect density. So, this study elaborates the growth optimization of AlGaN/AlN/Si (111) heterostructure with varied AlN buffer growth temperature (760 to 800 degrees C). It was observed that the remnant Al in low temperature growth of AlN buffer layer resist the growth quality of AlGaN epitaxial films. A highly single crystalline AlGaN film with comparatively lowest rocking curve FWHM value (similar to 0.61 degrees) and smooth surface morphology with least surface defect states was witnessed when AlN buffer was grown at 780 degrees C. From the Vegard's law, the photoluminescence analysis unveils Aluminium composition of 31.5% with significantly reduced defect band/NBE band ratio to 0.3. The study demonstrates good crystalline quality AlGaN film growth with Aluminium content variation between similar to 30-39% in AlGaN/AlN heterostructure on Si(111) substrate leading to a bandgap range which is suitable for next-generation solar-blind photodetection applications.