Abstract
The present work reports the synthesis of biomass derived activated carbon and its electrochemical behaviour in different electrolytes. Ricinus communis shell (RCS) was used as a raw material in this study for the synthesis of activated carbon (AC) following a high-temperature activation procedure using potassium hydroxide as the activating agent. The physical and structural characterization of the prepared Ricinus communis shell-derived activated carbon (RCS-AC) was carried by Brunauer-Emmett-Teller analysis, X-ray diffraction analysis, Fourier Transform Infrared Spectroscopy, Raman Spectroscopy and Scanning Electron Microscopy. The synthesized AC was electrochemically characterized using various techniques such as Cyclic voltammetry (CV), galvanostatic charge-discharge (GCD) tests, and Electrochemical impedance spectroscopy (EIS) measurements in different aqueous electrolytes (KOH, H2SO4, and Na2SO4). The results show that the double layer properties of the RCS-AC material in different electrolytes are distinct. In specific, the working electrode tested in 3 M KOH showed excellent electrochemical performance. It demonstrated a specific capacitance of 137 F g(-1) (at 1 A g(-1) in 3 M KOH) and exhibited high energy and power densities of 18.2 W hkg(-1) and 663.4 W kg(-1), respectively. The observed capacitance in 3 M KOH remains stable with 97.2% even after 5000 continuous charge and discharge cycles, indicating long-term stability. The study confirmed that the synthesized RCS-derived activated carbon (RCS-AC) exhibits good stability and physicochemical characteristics, making them commercially promising and appropriate for energy storage applications.