Abstract
Nano-sized Zr-Co doped nickel ferrites with nominal composition, NiZrxCoxFe2-2xO4 (x=0.0, 0.2, 0.4, 0.6, 0.8) were synthesized using the micro-emulsion route. The structural elucidation of the synthesized materials was carried out by X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy. The XRD analysis confirmed face centered cubic (FCC) structure of all compositions of NiZrxCoxFe2-2xO4 nanocrystallites. Crystallite size was calculated by Scherrer's formula found in the range 10–15nm. The variation in lattice parameter as determined by XRD data agreed with size variation of host (Fe3+) and guest (Zr4+ and Co2+) cations. FTIR spectra of doped NiFe2O4 exhibited the typical octahedral bands at 528.4cm−1 which is the characteristic feature of spinel structure of spinel ferrites. The characterized spinel NiZrxCoxFe2-2xO4 nano-ferrites were evaluated for their potential applications by magnetic hysteresis loops and dielectric measurements. The value of saturation magnetization (Ms) decreased from 47.9 to 13.09emu/g up to x=0.8 with ups and downs fluctuations in between x=0.0 to x=0.8. The high values of Ms of some compositions predicted the potential applications in high density perpendicular recording media and microwave devices. The frequency dependent behavior of permittivity (ε') is recorded and discussed with the help of hopping mechanism of both holes and electrons. The dielectric and magnetic data of NiZrxCoxFe2-2xO4 nano-ferrites suggested the potential applications of these ferrite nanoparticles in high frequency and magnetic data storage devices fabrication.
Zr-Co doped nickel nano-ferrites were prepared via micro-emulsion method. The crystallite size calculated by scherrer's formula lie in the range 10–15nm. The saturation magnetization decreases from 47 to 13emu/g up to x=0.8 with ups and downs fluctuations. The high values of coercivity and moderate saturation magnetization in some samples suggested their potential use in high density perpendicular recording media. [Display omitted]
•Micro-emulsion route was used to synthesize NiZrxCoxFe2-2xO4 nano-ferrites.•The crystallite size was found in the range 10–15nm.•The doping of Zr-Co optimized the coercivity (0.34T).•The coercivity indicated their use in high density perpendicular recording media.