Abstract
A copolymer of aniline (AN) and o-anisidine (OA), Poly(AN-co-OA) and its nanocomposite with ZnO nanoparticles, Poly(AN-co-OA)/ZnO were synthesized by chemical oxidative polymerization using ammonium persulfate as an oxidant in hydrochloric acid medium. The synthesized compounds were characterized using FTIR, XRD, SEM-EDS, TEM, and electrical conductivity techniques. The copolymer and nanocomposite were separately dissolved in N-methyl-2-pyrrolidone and were casted on low-carbon steel specimens using 10% epoxy resin as a binder. The anticorrosive properties of the coatings were studied in different corrosive environments such as 0.1 M HCl, 5% NaCl solution, and distilled water at a temperature of 30 A degrees C by conducting corrosion tests which include immersion test, open circuit potential measurements, potentiodynamic polarization measurements, and atmospheric exposure test. The surface morphology of the coatings prior to and after one-month immersion in corrosive solution was evaluated using SEM. It was observed that the nanocomposite coating exhibited higher corrosion resistance and provided better barrier properties in comparison with copolymer coating. The presence of ZnO nanoparticles improved the anticorrosion properties of copolymer coating in all corrosive media subjected to investigation.