Abstract
This work report was reported on the effect of the addition of organic filler, that is, 2(3), 9(10), 16(17), 23(24)-octahydroxycopper(II)phthalocyanine [(OH)(8)CuPc] (3), on the thermal, tensile, and morphological properties of a polyurethane matrix. The mechanical and dynamic mechanical thermal tests together with microstructural characterization of CuPc/PU composites were performed. The three PU composite films containing up to 1, 15, and 30 wt% of CuPc have different behaviors in terms of their morphological issues, thermal properties, and tensile behavior in comparison with the PU filmas the referencematerial. Very high elongations at break from 910% to 1230%, as well as high tensile strengths, illustrate excellent ultimate tensile properties of the prepared samples. The best mechanical and thermomechanical properties were found for the sample filled with 30 wt% of CuPc.