Abstract
Synthesis of flower-shaped ZnO nanostructures composed of hexagonal ZnO nanorods was achieved by the solution process using zinc acetate dihydrate and sodium hydroxide at very low temperature of 90
°C in 30
min. The individual nanorods are of hexagonal shape with sharp tip, and base diameter of about 300–350
nm. Detailed structural characterizations demonstrate that the synthesized products are single crystalline with the wurtzite hexagonal phase, grown along the [0
0
0
1] direction. The IR spectrum shows the standard peak of zinc oxide at 523
cm
−1. Raman scattering exhibits a sharp and strong E
2 mode at 437
cm
−1 which further confirms the good crystallinity and wurtzite hexagonal phase of the grown nanostructures. The photoelectron spectroscopic measurement shows the presence of Zn, O, C, zinc acetate and Na. The binding energy ca. 1021.2
eV (Zn 2p
3/2) and 1044.3
eV (Zn 2p
1/2), are found very close to the standard bulk ZnO binding energy values. The O 1s peak is found centered at 531.4
eV with a shoulder at 529.8
eV. Room-temperature photoluminescence (PL) demonstrate a strong and dominated peak at 381
nm with a suppressed and broad green emission at 515
nm, suggests that the flower-shaped ZnO nanostructures have good optical properties with very less structural defects.