Abstract
Natural fibers (NFs) have recently been the center of attention among researchers due to their low cost, availability, ease of manufacture, and potential environmental friendliness as reinforcing agents in composites. The present work deals with the mechanical behavior of palm fiber-reinforced epoxy-based composites with different weight percentage (Wt.%) ratios, ranging from 6% to 31.6%. Glass and hybrid fiber-reinforced epoxy-based composites were also examined. The indirect tensile test, i.e., diametral tensile test (DTT) and the small punch test (SPT), were used in the present work to determine the mechanical properties of the epoxy reinforced with discontinuous random oriented short fibers. Furthermore, short glass fibers were used to compare with palm fiber-reinforced epoxy. In addition, morphology observations of epoxy residue clinging to the natural fibers were carried out using the optical microscope and Scanning Electron Microscopy (SEM). The results showed that the natural fiber has a better adhesion bonding between the palm fiber/epoxy than that of glass fiber/epoxy. Therefore, adding palm fibers improves epoxy's mechanical properties compared with synthetic glass fibers. The composite with high Wt.% of NF showed the highest diametral tensile strength (DTS), 21.74 MPa, over other composites. The DTS of composites with medium and low Wt.% of NF was lower than that of the high Wt.% by 14% and 30%, respectively.