Abstract
Nuclear power facilities are being expanded to satisfy expanding worldwide energy demand. Thus, uranium recovery from secondary resources has become a hot topic in terms of environmental protection and nuclear fuel conservation. Herein, a mesoporous biosorbent of a hybrid magnetic-chitosan nanocomposite functionalized with cysteine (Cys) was synthesized via subsequent heterogeneous nucleation for selectively enhanced uranyl ion (UO22+) sorption. Various analytical tools were used to confirm the mesoporous nanocomposite structural characteristics and confirm the synthetic route. The characteristics of the synthesized nanocomposite were as follows: superparamagnetic with saturation magnetization (Ms: 25.81 emu/g), a specific surface area (S-BET: 42.56 m(2)/g) with a unipore mesoporous structure, an amine content of similar to 2.43 mmol N/g, and a density of similar to 17.19/nm(2). The experimental results showed that the sorption was highly efficient: for the isotherm fitted by the Langmuir equation, the maximum capacity was about 0.575 mmol U/g at pH range 3.5-5.0, and Temperature (25 +/- 1 degrees C); further, there was excellent selectivity for UO22+, likely due to the chemical valent difference. The sorption process was fast (similar to 50 min), simulated with the pseudo-second-order equation, and the sorption half-time (t(1/2)) was 3.86 min. The sophisticated spectroscopic studies (FTIR and XPS) revealed that the sorption mechanism was linked to complexation and ion exchange by interaction with S/N/O multiple functional groups. The sorption was exothermic, spontaneous, and governed by entropy change. Desorption and regeneration were carried out using an acidified urea solution (0.25 M) that was recycled for a minimum of six cycles, resulting in a sorption and desorption efficiency of over 91%. The as-synthesized nanocomposite's high stability, durability, and chemical resistivity were confirmed over multiple cycles using FTIR and leachability. Finally, the sorbent was efficiently tested for selective uranium sorption from multicomponent acidic simulated nuclear solution. Owing to such excellent performance, the Cys nanocomposite is greatly promising in the uranium recovery field.