Abstract
The failed gas-turbine blades (first stage blades) (type Siemens V94.2 KWU) were acquired from TNB Research Sdn. Bhd: a subsidiary of Malaysian power-generation industry (TNB, Malaysia). The blades were sectioned for metallographic investigations. The microstructural characterization involved use of both optical as well as electron microscopes including application of EPMA technique. The Microstructures were compared for three spots selection i.e
. leading edge of the blade (transverse and longitudinal), trailing edge of the blade (transverse and longitudinal), and centre (near the platform of the blade) (transverse and longitudinal). The material properties and behavior at high temperature were interpreted on the basis of the observed microstructures and the phases present in the alloy. The interpretations were related to the operating conditions of the turbine blade; and main cause of failure was found to be creep damage. Recommendations have been made for improved material performance.