Abstract
Polyamide thin-film composite (TFC) was fabricated on polysulfone (PS-20) base by interfacial polymerization of aqueous
m
-phenylenediamine (MPD) solution and 1,3,5-benzenetricarbonyl trichloride (TMC) in hexane organic solution. Multi-wall carbon nanotubes (MWCNT) were carboxylated by heating MWCNT powder in a mixture of HNO
3
and H
2
SO
4
(1:3 v/v) at 70 °C under constant sonication for different periods. Polyamide nanocomposites were prepared by incorporating MWCNT and the carboxylated MWCNT (MWCNT–COOH) at different concentrations (0.001–0.009 wt%). The developed composites were analyzed by Fourier transform infrared spectroscopy-attenuated total reflection, scanning electron microscopy, transmission electron microscopy, contact angle measurement, determination of salt rejection and water permeate flux capabilities. The surface morphological studies displayed that the amalgamation of MWCNT considerably changed the surface properties of modified membranes. The surface hydrophilicity was increased as observed in the enhancement in water flux and pure water permeance, due to the presence of hydrophilic nanotubes. Salt rejection was obtained between 94 and 99% and varied water flux values for TFC-reference membrane, pristine-MWCNT in MPD, pristine-MWCNT in TMC and MWCNT–COOH in MPD were 20.5, 38, 40 and 43 L/m
2
h. The water flux and salt rejection performances revealed that the MWCNT–COOH membrane was superior membrane as compared to the other prepared membranes.