Abstract
Polar-nonpolar silicone materials of different morphology and composition were investigated by means of broadband dielectric relaxation spectroscopy in order to elucidate the effect of polar content and nature of the interface on the segmental mobility of polydimethylsiloxane (PDMS) chains. The variation of dielectric parameters with temperature revealed two distinct alpha-relaxations corresponding to dynamic glass transitions of the components, while another polarization phenomenon was evidenced due to accumulations of charges at the interphases between the two polymers with different electrical properties. It was found that the secondary beta-relaxation was favored by the increased content of polar groups, while this parameter had the reverse influence on both alpha(PDMS) and alpha(P62), restricting the PDMS chain segment mobility. The activation energy of the interfacial polarization decreased with the polarity, showing increased mobility of charge carriers and less restriction to the interfacial polarization. (C) 2018 Elsevier Ltd. All rights reserved.