Abstract
Three different samples were synthesized based on polyepoxide resin, a solidifying agent, and a Bi2O3 doping compound. The polyepoxide resin and solidifying agent were added in a 2:1 ratio by weight and the Bi2O3 compound was added in ratios of 0, 5, and 10 wt. %. The density of the synthesized composites was measured using an MH-300A densimeter with an uncertainty in measurement of 0.001 g/cm(3). The measurements showed that the density of the fabricated composite varied from 1.103 g/cm(3) to 1.20 g/cm(3) when the reinforcing Bi2O3 compound was raised from 0 wt. % to 10 wt. %. Furthermore, the gamma-ray shielding parameters were evaluated based on the simulated mean track length of gamma-photons inside the synthesized composites using MCNP-5 code. The simulated results show an enhancement in the shielding parameter when increasing the Bi2O3 concentration, where the linear attenuation coefficient values increased from 0.101 cm(-1) to 0.118 cm(-1) as the Bi2O3 concentration increased from 0 to 10 wt. %. The increase in the LAC has a positive effect on the other shielding properties.