Abstract
Morphological analysis of the nanocomposites showed that multi-wall carbon nanotubes were uniformly distributed in polypropylene. Nanoindentation creep and nano-impact tests were carried out. Several equations/models were used to analyze creep data. From creep test, hardness of the nanocomposites increased by 18 and 36% for C150P and C70P, respectively, compared to polypropylene, whereas elasticity also increased by 20 and 34%. From nano-impact test, hardness of the nanocomposites was also higher than that of neat polypropylene. However, hardness (dynamic/impact) values were slightly higher than the (quasi-static) hardness resulted from creep test. In addition, degree of crystallinity of nanocomposites also increased by 12.6 and 14.3%.