Abstract
Fe-rich amorphous dust core alloys with minor-addition of Mo and/or Cr were synthesized because of the industrial request of mass production of high efficient low core loss Fe-based dust cores. It was found that the present Fe-(Cr, Mo)-P-B-Si-(C) amorphous alloy ribbons exhibit good soft magnetic properties of above 1.5 T for saturation magnetization, below 10 A/m for coercivity and rather good corrosion resistance in 3%NaCi aqueous solution. Besides, the amorphous alloy ribbons exhibit good bending ductility in as-spun and optimally annealed states. It is noticed that these characteristics are much superior to those for commercial Fe-Cr-Nb-P-B-Si soft magnetic dust core alloy (SENNTIX). In addition, the annealing treatment was noticed to cause the improvement of corrosion resistance without detriment to bending ductility. The new Fe-based soft magnetic alloys with good combined characteristics are expected to be used as the basic material as high-efficient soft magnetic dust cores in a high frequency range. (C) 2016 Published by Elsevier Ltd.