Abstract
In this study, we investigate noble metal free photocatalytic water splitting on natural anatase single crystal facets and on wafer slices of the [001] plane before and after these surfaces have been modified by high pressure hydrogenation and hydrogen ion-implantation. We find that on the natural, intact low index planes, photocatalytic H-2 evolution (in the absence of a noble metal co-catalyst) can only be achieved when the hydrogenation treatment is accompanied by the introduction of crystal damage, such as simple scratching and miscut in the crystal, or by implantation damage. X-ray reflectivity, Raman, and optical reflection measurements show that plain hydrogenation leads to a approximate to 1 nm thick black titania surface layer without activity, while a colorless, density modified, and approximate to 7 nm thick layer with broken crystal symmetry is present on the ion implanted surface. These results demonstrate that (i) the H-treatment of an intact anatase surface needs to be combined with defect formation for catalytic activation and (ii) activation does not necessarily coincide with the presence of black color. Published by AIP Publishing.