Abstract
The influence of the concentration of adenine (AD), as a safe inhibitor, on the corrosion of low carbon steel (LCS) in aerated 4.0 M H2SO4 solutions was studied. The investigations involved weight loss, potentiodynamic polarization, impedance and electrochemical frequency modulation (EFM) methods. Variations of open-circuit potential (OCP) as a function of time till steady-state potentials were also studied. Measurements were conducted under the influence of various experimental conditions complemented with ex situ EDX examinations of the electrode surface. By using EFM measurements, corrosion current density was determined without prior knowledge of Tafel slopes. Results obtained revealed that together with iodide ion, AD is an effective corrosion inhibitor for LCS corrosion in H2SO4 solutions. Synergism between iodide ion and AD was proposed. Potentiodynamic polarization studies showed that AD alone and the mixture of AD and iodide ions act as mixed-type inhibitors for the corrosion of LCS in 4.0 M H2SO4 solution. The inhibition mechanism involves the electrostatic adsorption of protonated AD molecules on the LCS surface charged with a negative layer of chemisorbed I- ions. An adherent layer of inhibitor is postulated to account for the protective effect. EDX examinations of the electrode surface confirmed the existence of such adherent layer on the electrode surface. The inhibition efficiency increases with increase in the concentration of AD and immersion time. The potential of zero charge (PZC) of the LCS electrode was determined in 4.0 M H2SO4 solutions in the absence and presence of 0.001 M Kl, and the mechanism of adsorption was discussed. The results obtained from chemical and electrochemical measurements were in good agreement. (C) 2008 Elsevier Ltd. All Fights reserved.