Abstract
[Display omitted]
•High quality of the PFO/CsPbBr3 QDs thin films were synthesized.•Insignificant chemical interaction was observed between the CsPbBr3 QDs and PFO.•Direct and indirect band gap of the PFO reduced with increasing CsPbBr3 QDs content.•Non-radiative energy transfer from PFO to CsPbBr3 QDs was detected.
The aim of this study is to investigate the optical and structural properties of polymer/perovskite quantum dots (QDs) composite thin films and estimate the applicability of using these blends as active materials in photonic devices. A solution has been utilized, which is processed based on conjugated polymer and perovskite QDs composite films. The incorporation of CsPbBr3 QDs, with various weight ratios, influences the structure of the thin films, as proven by several techniques. The results of the study showed that the surface of the poly(9,9-di-n-octylfluorenyl-2,7-diyl) (PFO)/CsPbBr3 thin films improved, when compared to that of the pristine CsPbBr3 thin film. The increase in the steepness parameter and decrease in both the energy gaps and Urbach tail, upon the increment of CsPbBr3 QDs, can be attributed to the decrease in the localized density of electronic states within the forbidden band gap of the hybrids. The overlap between the absorption spectrum of PFO and emission spectrum of CsPbBr3 QDs, and the enhancement in the emission peak of CsPbBr3 in the blends, confirmed the efficient non-radiative energy transfer between them.