Abstract
This study presents the fabrication and investigation of humidity sensors based on orange dye (OD) and polyaniline (PANI) composite films. A blend of 3 wt.% OD with 1 wt.% PANI was prepared in 1 ml water. The composite films were deposited on glass substrates between pre-deposited silver electrodes. The gap between the electrodes was 45 mu m. The sensing mechanism was based on the impedance and capacitance variations due to the absorption/desorption of water vapor. It was observed that with the increase in relative humidity (RH) from 30% to 90%, the impedance decreases by 5.2x10 super(4) and 8.8x10 super(3) times for the frequencies of 120 Hz and 1 kHz, respectively. The impedance-humidity relationship showed a more uniform change compared to the capacitance-humidity relationship in the RH range of 30% to 90%. The consequence of annealing, measuring frequency, response and recovery time, and absorption-desorption behavior of the humidity sensor were also discussed in detail. The annealing resulted in an increase in sensitivity of up to 2.5 times, while the measured response time and recovery time were 34 s and 450 s, respectively. The impedance-humidity relationship was simulated.