Abstract
[Display omitted]
•Mn-doped PAN nanofibers were decorated with ZIF-67.•Oriented attachment of PVP/ZIF-67 occurred on Mn-doped PAN-2MI nanofibers.•PVP/ZIF-67/Mn-fibers carbonized at 900 ℃ resulted in flexible C/Co-CoOx/Mn-CNF.•The areal capacitance of 1263 mF·cm−2 was obtained at a current density of 0.25 mA·cm−2.•The energy density of 0.18 mWh·cm−2 was obtained at a power density of 0.5 mW·cm−2.
Electrodes for flexible supercapacitors were fabricated from manganese-doped carbon nanofibers (Mn-CNF) decorated with carbon-coated Co-CoOx (C/Co-CoOx) nanotubes. The Mn-doped polyacrylonitrile (PAN)–2-methylimidazole (2MI) solution was electrospun using optimized Mn concentrations and ZIF-67 was then surface loaded by wet impregnation with added polyvinylpyrrolidone (PVP). These ZIF-67 loaded Mn-fibers, when annealed, resulted in carbon-coated C/Co-CoOx nanotubes on the Mn-CNF surface. In the presence of PVP, ZIF-67 oriented attachment occurs, forming evenly dispersed CoOx particles even after high temperature annealing. XRD spectra exhibit the formation of metallic Co nanoparticles (NPs), whereas Raman spectra and XPS indicate Co particle oxidation. A carbon coating limits the oxidation of Co; thus, the particles are called C/Co-CoOx. A symmetric supercapacitor cell prepared using the CNFs decorated with C/Co-CoOx using an aqueous electrolyte has a capacitance of 1263 mF⋅cm−2 at a current density of 0.25 mA⋅cm−2 and a wide potential window of 1.4 V for the optimal case. Long-term cycling showed 110 % capacitance retention after 10,000 cycles. Moreover, bending tests and powering LEDs demonstrated the flexibility and improved charge storage of the prepared nanofiber electrodes.