Abstract
A low visible light absorption efficiency and high recombination rate of photogenerated charge carriers are two major problems encountered in graphitic carbon nitride (g-C3N4) based photocatalysts for water splitting applications. In this work, Pd-Ag bimetallic and monometallic nanoparticles were decorated on graphitic carbon nitride by a simple chemical reduction method and evaluated for their ability to produce H-2 during water splitting reactions. The physical and photophysical characteristics of the as-prepared Pd-Ag/g-C3N4 photocatalysts were studied by powder X-ray diffraction (PXRD), UV-visible diffuse reflection spectroscopy (DRS), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), energy dispersive spectroscopy (EDS) and steady state photoluminescence (PL). The Pd-0.7-Ag-0.3/g-C3N4 photocatalyst with an overall metal loading of 1 wt% showed a very high H2 generation rate of 1250 mu mol h(-1) g(-1), which is 1.5 and 5.7 times higher than those of the Pd/g-C3N4 and Ag/g-C3N4 photocatalysts, respectively. The high activity of the Pd-Ag/g-C3N4 photocatalyst was attributed to the inherent property of palladium metal to quench photogenerated electrons by the Schottky barrier formation mechanism and strong visible light absorption due to the characteristic surface plasmon resonance (SPR) of silver nanoparticles along with the absorption of g-C3N4.