Abstract
This paper investigates the residual tensile properties of newly developed glass fiber reinforced polymer (GFRP) bars after being subjected to elevated temperatures for different periods. A total of 120 GFRP specimens were tested in this study. Half of the samples were covered with concrete while the other half were bare bars. The specimens were subjected to three different controlled temperatures (100, 200 and 300 degrees C) for three different periods (1, 2, and 3 h). Test results showed chat almost no losses were observed in the tensile modulus after all exposure periods and temperatures. Losses in the tensile strength, proportional to the level of temperature and exposure period, were recorded. The bars with concrete cover showed higher residual tensile strength compared to their counterparts without coating. The concrete cover was more effective at the lowest temperature level (100 degrees C) and at the shortest time period (1 h). Scanning Electronic Microscopy (SEM) technique was also used to investigate the effect of elevated temperature on the degradation mechanism of the GFRP bars. The results showed that increasing the temperature level affected the resin matrix surrounding the glass fibers and consequently affected the bond between the fibers and the matrix. (C) 2012 Elsevier Ltd. All rights reserved.