Abstract
Semiconductor nanoparticles and nanocrystals have a great impact due to its contribution in the diverse fields including electronics, solar energy, biological imaging, and photonics. Among these semiconductor nanoparticles, cadmium selenide of II-VI group binary semiconductor nanoparticles were synthesized using solvothermal process for the different reaction temperatures. The XRD pattern of the synthesized samples confirms the crystalline nature of the samples and showed increase in its crystallite size with rise in temperature. The morphology of the samples was analysed with TEM images and found that the nanoparticles synthesized at different temperatures were varied in size and shape indicating the increase in the size of the particles with the raise in temperature. The optical properties of the samples pointed out that they exhibit a blue shift owing to quantum confinement. Photocatalytic activity was carried out for the synthesized samples under visible light radiation using methylene blue (MB) as a model pollutant and it proved to be a good photocatalyst achieving the efficiency of 75% which is promising for future application with good optimization. The efficiency could be increased when these semiconductor CdSe nanoparticles are doped with metal particles due to an increase in the absorption edge wavelength and a decrease in bandgap energy were reported in detail.
•CdSe nanoparticles were synthesized using solvothermal process.•Reaction temperature increases at higher temperature showed a rod-like morphology.•75% of photo-degradation of methylene blue in water with in 180 min.•Develop methods for the textile wastewater effluents at low cost.•And proves to be efficient method as it does not produce any secondary pollutants.